Henan Sinmat Chemical Co., Ltd. ke e mong oa bahlahisi ba tšepahalang ka ho fetisisa le bafepedi ba al2o 3 30%-50% inert ceramic bolo ka China. Ka phihlelo e ntši, re go amogela ka borutho go reka boleng bjo bo phagamego bja al2o3 30%-50% inert ceramic ball yeo e rekišwago mo go tšwa feketoring ya rena. Ikgokaganye le rena bakeng sa sampole ya mahala.
Matseno
30%-50% ya dibolo tša ceramic tše di sa šomego tša alumina, ka tlwaelo di bitšwa dibolo tša ceramic tša magareng-alumina tše di sa šomego goba dibolo tša ceramic tša magareng-alumina tše di thekgwago. Ke mohuta wa sedirišwa sa go tlatša sa sebopego sa ceramic sa maemo a magareng seo se theilwego godimo ga tshepedišo ya alumina-silicate, yeo e godišago kudu dithoto tša metšhene le tša phišo ka go oketša diteng tša alumina.
30%-50% alumina inert ceramic dibolo di phahame haholo ho motheo kapa mahareng-tlaase alumina dibolo ceramic ka dipehelo tsa matla, thempereichara ho hanyetsa le bophelo ba tšebeletso, ha bona e le tlaase haholo ho feta ea phahameng-alumina ceramic dibolo. 30%-50% alumina inert ceramic dibolo, ke tse ngata sebediswa ka sehloohong tšehetsa dibolo ceramic ka mokgwa wa intasteri, gomme di loketše ka mo go swanetšego bjalo ka "legato le legolo la go rwala morwalo" ka tlase ga tora.
Bjalo ka dibolo tša ceramic tše di šomišwago kudu tša magareng-alumina tše di thekgwago ka dipolanteng tša intasteri, 30%-50% ya dibolo tša ceramic tše di sa šomego tša alumina di kopanya maatla, go ganetša themperetšha, le ekonomi, gomme di na le go fetofetoga mo go tiilego le maemo a tshepedišo. Ke lintho tse bonahalang motheo motheo bakeng sa tshebetso tsitsitseng nako e telele ya dithulaganyo catalytic le adsorption.
Tlhaloso ya Sethekniki
|
Mohuta |
30%-50% alumina inert ceramic bolo |
|
|
Ponagalo ya go bonagala |
Bolo ye tšhweu |
|
|
AL2O3+SiO2(%) |
>93 |
|
|
AL2O3(%) |
30-50 |
|
|
Fe2O3(%) |
<1 |
|
|
CaO (%) 1.1. |
<2 |
|
|
MgO (%) . |
<0.5 |
|
|
TiO2(%) |
<0.1 |
|
|
K2O+Na2O(%) |
<3.5 |
|
|
H2O Go monya(wt.%) . |
<1 |
|
|
Bongata segokanyipalo(g / ml) . |
1.35-1.65 |
|
|
Mohs Thata(sekala) . |
>7 |
|
|
Kganetšo ya Mogote(℃) . |
>1500 |
|
|
Kganetšo ya Esiti(%) . |
>98 |
|
|
Kganetšo ya Alkali(%) . |
>85 |
|
|
Matla a go pšhatlaganya(KN) . |
1/4 intshi (6mm) . |
>0.56 |
|
1/2 intshi (13mm) . |
>1.56 |
|
|
3/4 ka intshi (19mm) . |
>2.89 |
|
|
1 intshi (25mm) . |
>4.89 |
|
|
1-1/2 ka intshi (38mm) . |
>5.33 |
|
|
2 ka intshi (50mm) . |
>6.22 |
|
Kgopelo
- Go Hlwekiša Oli Le Tshepetšo ya Gase ya Tlhago
- Monya Goba Karabelo Tower Media
-
Thekgo ya Bethe ya Sehlohleletši sa Petrokhemikhale
Dithegi tše di fišago .: Al2O 3 30%-50% e sa sebetseng bolo ea ceramic, 30% 50% alumina bolo e sa sebetseng ceramic, Al2O3 30% 50% bolo ea ceramic, 30% 50% bolo e sa sebetseng ceramic, 30% 50% alumina bolo ea ceramic, China Al2O3 30%-50% baetsi ba bolo ea ceramic e sa sebetseng, baabi