Ke Eng Silica Alumina Ratio Ya Zeolite Molekyule Sieve?

The silika alumina karo-karolelano (SiO₂/AlO₃molar karo-karolelano) ke senotlolo taolo paramethara bakeng sa tshebetso konokono ya zeolite limolek'hule sieves, ka ho toba susumetsa bona tlhako botsitso, acid sebaka kabo, le pore topology. A re ithute ka mofuta-dimelo, sebopego-kamano ya tshepedišo ya disefo tša dimolekule tša zeolite tšeo di nago le dikarolwana tša aluminiamo tše di fapanego tša silicon-, gammogo le go sepelelana ga tšona ga tirišo ka dikhemikhale tša petroleum, tšhireletšo ya tikologo, bj.bj.

Tlhaloso Ya Silica Alumina Ratio

• Tekanyo ya alumina ya silika e šupa tekanyo ya molar goba tekanyo ya athomo (Si/Al) ya silicon-oxygen tetrahedron (SiO₄) go ya go aluminiamo-tetrahedron ya oksitšene (AlO₄) ka gare ga tlhako ya sefe ya dimolekule. Gomme boleng bja yona bo laola segokanyipalo sa tefo ya tlhako, le tsela ya diputseletšo tša cation.
• Tlase silica alumina karo-karolelano limolek'hule sefe e na le phahameng mpe mpe tefo segokanyipalo ka tlhako, 'me hloka palo e khōlō ea cation compensation. Tlhako ya sefe ya dimolekule ya tekanyo ya alumina ya silika ye e phagamego e laolwa ke ditlemo tše maatla tša Si - O- Si, gomme sebopego sa yona sa topological se tsepame kudu ka phišo. Tekanyo ya silica alumina e laola maatla a esiti, kabo ya bogolo bja pore le hydrophobicity ya sefe ya dimolekule, e dira gore e lokele maemo a go fapana a intasteri.

Classification Ya Zeolite Molekhule Sefo

Mokgwa wa Taolo Wa Silica Alumina Ratio

• Taolo ya esiti: Diathomo tša aluminiamo ke mothopo wa mafelo a esiti ya Brønsted, gomme tekanyo ya alumina ya silika e ama ka go lebanya segokanyipalo sa esiti le maatla: Ge tekanyo ya alumina ya silika e oketšega go tloga go 20 go ya go 150, palomoka ya mafelo a esiti a fokolago (desorption ka 120℃) le mafelo a esiti a maatla (desorption ka 400℃) ya HZSM-5 e fokotšega ka 40%. Karolo ya mafelo a esiti ye maatla ka tekanyo ya godimo ya alumina ya silika (go swana le ZSM-5-300) e a fokotšega, e thibela karabelo ya lehlakore la phetišetšo ya hydrogen, gomme go kgetha ga propylene go oketšega go fihla go 81.5%.
• Sebopego sa pore le tshepedišo ya adsorption: Ge tekanyo ya alumina ya silica ya sefe ya dimolekule ya ZSM-22 e oketšega go tšwa go 40 go ya go 130, bophagamo bja pore bo thoma ka go oketšega go fihla go 0.25 cm³/g gomme ka morago e fokotšega go fihla go 0.18 cm³/g, because the framework shrinkage is aggravated under high silicon conditions. ZSM-5 molecular sieve with a silica alumina ratio of >100 e na le bokgoni bja go monya bja 41 mg/g bja toluene, yeo e lego 70% ye e phagamego go feta ya ZSM-5 ka tekanyo ya silica alumina ya 38, ka lebaka la gore hydrophobicity ye e okeditšwego e fokotša go monya ga phadišano ga dimolekule tša meetse.
• Botsitso bja phišo le go swarelela ga phišo ya meetse: Mohuta wa fase - silicon Y - (SiO₂/Al₂O₃=2) e feta go phuhlama ga marapo ka 660℃, mola e le godimo-silicon ZSM-5 (SiO₂/Al₂O₃>30) e ka kgotlelela dithemperetšha tša go fihla go 900℃. Ge tekanyo ya alumina ya silica ka gare ga sešušumeletši sa Cu/SSZ-13 e oketšega go tšwa go 6 go ya go 16, seelo sa go boloka mošomo wa SCR se oketšega go tloga go 45% go ya go 85% ka morago ga kalafo ya hydrothermal ka 800℃/16h, ka lebaka la go fokotšega ga seelo sa dealumination.

Silica Alumina Ratio Adaptation Leano Ka Ditirišo tša Intasteri

• Fluid catalytic cracking (FCC): Ge tekanyo ya silica alumina ya USY molecular sieve e le 6-8, go kgetha ga coke go fokotšega ka dintlha tša phesente tše 2.5 gomme poelo ya oli ye bofefo e oketšega ka 3%.
• Methanol go olefins (MTO): Ge tekanyo ya alumina ya silika ya sefe ya dimolekule ya SAPO-34 e le 0.3-0.5, kgetho ya ethylene/propylene e fihla go 80%. Tekanyo ya alumina ya silika ye e phagamego kudu e akgofiša go bewa ga khapone ya dikhaponetaeoksaete tša monkgo wa polycyclic gomme e hlola go se šome.
• VOCs adsorption: Bokgoni bja go monya bja sefe ya dimolekule ya ZSM-5 ka tekanyo ya silica alumina ya 300 bakeng sa letoto la benzene ke 120 mg/g, gomme nako ya go tsenelela e atološitšwe go fihla go 66 min, yeo e lego kaone go feta 40 mg/g ya khapone ye e šomišitšwego.
• NOx tloso: Ha silica alumina karo-karolelano ya Cu / LTA catalyst ke 16-23, NOx phetolo sekhahla lula ka 90% ka mor'a hydrothermal botsofali ka 600℃, e leng na le bobeli mosebetsi phahameng le tšoarellang.
• Laoloa lithethefatsi lokolloa: Low silica alumina karo-karolelano (1.5 ~ 2.0) mofuta A zeolite limolek'hule sefe finyella lokolloa tšoarellang ea ibuprofen ka pore boholo taolo, le 24h lokolloa sekhahla sa 95%.
• CO₂go swara: Amine - funnctionalized mofuta X zeolite dimolekule sefe (silica alumina karo-karolelano 2.5) boloka e CO₂adsorption bokgoni ba 12 wt% tlas'a maemo a mongobo, 'me ho hanyetsa lona metsi e eketsehile ka makhetlo a 3.